TRANSLUCENT PVC COMPOUND FOR CABLE AND WIRE

1.Translucent pvc granules for cable and wire 2.High temperature flexibility 3.Flame retardant 4.Customized formulation

1,For our PVC compound products, PVC resin is the main raw material. And adding plasticizer, stabilizer, colorants and other additives , processed by mixing ,extruding and granulating. We have advanced technology, good plasitcization and stable performance. Our products mainly used for the elevator, electric welding machine, driving and outdoor portable electric wire and cable security lay

2,Use and standard: meet enterprises standard Q / 320287 NMM01-2008, used for elevator, electric welding machine, driving and outdoor portable electric wire and cable, conform to the corresponding cable specification.

3,Process: extrusion and injection

4,Appearance: cylindrical particles,  plastication should be good, the color and luster is even, without obvious impurity.

5,Packing: 25kg net weight per in a kraft bag with insider PE bag

6,Transportation and storage: this kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.

 

We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting  compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.Our products can fit the ROHS directive, REACH,non-PAHS, ,ASTM standard and etc.

                                                PVC COMPOUND SPECIFICATION

Description index	TYPE
	J-70	JR-70	H-70	HR-70	JGD-70	HI-90	HII-90	J-90
TensileStrength(before ageing) / MPa ≥	15.0	15.0	15.0	12.5	16.0	16.0	16.0	16.0
Elongation at rupture (before ageing) / %>	150	180	180	200	150	180	180	150
TensileStrength (after ageing) / Mpa ≥	15.0	15.0	15.0	12.5	16.0	16.0	16.0	16.0
Elongation at rupture (after ageing) / %  >	150	180	180	200	150	180	180	150
Thermal Stability (at 200 °C) / min ≥	60	50	50	65	100	80	180	180
Volume electric resistance (at 20°C)≥	1.0*1012	1.0*1011	1.0*108	1.0*108	3.0*1012	1.0*109	1.0*109	1.0*1012
Volume electric resistance (at working temperature) / m≥	70    °C	70    °C	-	-	70    °C	-	-	95    °C
	1.0*109	1.0*109	-	-	5.0*109	-	-	5.0*108
Loss of  Mass (at 100     °C) / g/m2 ≤	168h	168h	168h	168h	168h	240h	240h	240h
	20	20	23	25	20	15	20	20
Fragility temperature°C	-15	-20	-25	-30	-15	-20	-20	-15
Colour Shade	SHALL MATCH

 

TRANSLUCENT PVC COMPOUND FOR CABLE AND WIRE